experiment.yaml

material:
    name: Cu-110
    surface_plane: [1, -1, 0]
    atomic_mass: 63.546 # g mol^-1
    mass_density: 8912.9293 # kg m^-3
    yield_strength: 248.2113 # MPa
    elastic_modulus: 117.21 # GPa
    poisson_ratio: 0.34
    C11: 169.1 # GPa
    C12: 122.2 # GPa
    C44: 75.4 # GPa

tgs:
    cooldown:
        path: data/tgs/cooldown
        temperature_path: data/temperature/Cu_temperature.csv
        grating: 3.5276 # µm
    irradiation:
        path: data/tgs/irradiation
        srim_path: data/srim/VACANCY.txt
        grating_spacing: 3.5276 # µm
        start_current: 1.0e-9 # A
        end_current: 0.1e-9 # A
        ion_charge: 6 # e
        beam_aperture: 2.00 # mm
        duration: 1800 # s

temperature:
    ref_path: data/temperature/ref.csv
    ref_offset: 1200 # s
    tgs_path: data/temperature/tgs_ion.csv
    tgs_offset: 2400 # s
    ion_path: data/temperature/tgs_ion.csv
    ion_offset: 14400 # s
    ref_tgs_duration: 11700 # s
    ion_duration: 2400 # s
    zoom_duration: 2471 # s

heat_load:
    cryohead_path: data/cryohead
    values:
        k_steel: 16.3  # W m^-1 K^-1
        k_ceramic: 1.46  # W m^-1 K^-1
        L^stage_steel: 0.04  # m
        A^stage_steel: 7.854e-5  # m^2
        L^stage_ceramic: 0.08  # m
        A^stage_ceramic: 7.85e-5  # m^2
        L^gimbal_steel: 0.076  # m
        A^gimbal_steel: 3.50e-5  # m^2
        L^axis_ceramic: 0.015  # m
        A^axis_ceramic: 6.57e-5  # m^2
        T_A: 298  # K
        S: 0.121  # m^2
        sigma: 5.67e-8  # W m^-2 K^-4
        epsilon: 0.16
        P_tgs: 3.66e-3  # W
        E_ion: 12.4e+6  # eV
        I_ion: 4.5e-10  # A
        C: 1.25 # W K^-1